* Plate, Strip, and Sheet *
- 순수 티타늄

규격	Grade	화학성분(Max. %)						기계적성질
		N	C	H	Fe	O	Ti	인장강도			내력(0.2% offset)			신 율 (%)
		N	C	H	Fe	O	Ti	kgf/ mm2	Ksi	Mpa (N/mm2)	kgf/ mm2	Ksi	Mpa (N/mm2)	신 율 (%)
ASTM B265	Grade1 Grade2 Grade3 Grade4	0.03 0.03 0.05 0.05	0.10 0.10 0.10 0.10	0.015 0.015 0.015 0.015	0.20 0.30 0.30 0.50	0.18 0.25 0.35 0.40	잔량	>=25 >=35 >=46 >=56	>=35 >=50 >=65 >=80	>=240 >=345 >=450 >=550	18-32 28-46 39-56 49-67	25-45 40-65 55-80 70-95	17-310 275-450 380-550 485-655	>=24 >=20 >=18 >=15
ASME SB- 265	Grade1 Grade2 Grade3	0.03 0.03 0.05	0.10 0.10 0.10	0.015 0.015 0.015	0.20 0.30 0.30	0.18 0.25 0.35	"	>=25 >=35 >=46	>=35 >=50 >=65	>=240 >=345 >=450	18-32 28-46 39-56	25-45 40-65 55-80	170-310 275-450 380-550	>=24 >=20 >=18
MIL-T -9046	CP-1 CP-2 CP-3 CP-4	0.05 0.05 0.05 0.05	0.08 0.08 0.08 0.08	0.015 0.015 0.015 0.015	0.50 0.30 0.30 0.20	0.40 0.30 0.20 0.15	"	>=56 >=42 >=35 >=25	>=80 >=60 >=50 >=35	>=552 >=414 >=345 >=241	49-67 39-56 28-46 18-32	70-95 55-80 40-65 25-45	483-655 379-552 276-448 172-310	>=15 >=18 >=20 >=24
AMS 4902	40,000psi Y.S 55,000psi Y.S 70,000psi Y.S	0.05 0.05 0.05	0.08 0.08 0.08	0.0125 0.015 0.015	0.50 0.50 0.50	0.20 0.30 0.40	"	>=35 >=46 >=56	>=50 >=65 >=80	>=345 >=450 >=550	28-46 39-56 49-67	40-65 55-80 70-95	276-448 380-550 485-655	>=20 >=18 >=15
DIN 17860	3.7025.10 3.7035.10 3.7055.10 3.7065.10	0.05 0.06 0.06 0.07	0.08 0.08 0.10 0.10	0.013 0.013 0.013 0.013	0.20 0.20 0.30 0.35	0.10 0.20 0.25 0.30	"	30-42 40-55 47-60 55-75	42-59 57-78 67-86 78-107	290-410 390-540 460-590 540-740	>=18 >=25 >=33 >=40	>=26 >=36 >=46 >=57	>=180 >=250 >=320 >=390	>=25 >=20 >=16 >=15
JIS H4600	Class1 Class2 Class3	0.05 0.05 0.07	- - -	0.013 0.013 0.013	0.15 0.20 0.30	0.15 0.20 0.30	"	28-42 35-52 49-63	40-60 50-74 70-90	275-412 343-510 481-618	>=17 >=22 >=35	>=24 >=31 >=50	>=167 >=216 >=343	>=27 >=23 >=18

- 합금 티타늄

규격

Grade

화학성분(%)

기계적 성질(소둔)

인장강도

내력

신율(%)

Mpas
(N/mm2)

Mpa
(N/mm2)

ASTM
B265

Grade5
Grade7
Grade11

0.05
<=0.03
<=0.03

0.10
<=0.10
<=0.10

0.015
<=0.015
<=0.015

0.40
<=0.30
<=0.20

0.20
<=0.25
<=0.18

5.5-6.75

3.5-4.5

0.1-0.25
0.12-0.25

잔량

895
<=345
<=240

830
275-450
170-310

10
<=20
<=24

JIS H4607
JIS H4605

Class60
Class11
Class12
Class13

0.05
<=0.05
<=0.05
<=0.07

0.10
-
-
-

0.015
<=0.013
<=0.013
<=0.013

0.30
<=0.25
<=0.25
<=0.30

0.20
<=0.15
<=0.20
<=0.30

5.5-6.75

3.5-4.50

0.1-0.25
0.12-0.25
0.12-0.25

잔량

890-920
275-412
343-510
481-618

825-865
<=167
<=216
<=343

10
<=27
<=23
<=18

* Bar -
- 순수 티타늄

규격	Grade	열처리 조건	단면두께	기계적 성질
				인장강도
				kgf/mm2	Kai	Mpa(N/mm2)
ASTM B348	Grade1 Grade2 Grade3 Grade4	소 둔 소 둔 소 둔 소 둔	5/16"-4-1/2" 5/16"-4-1/2" 5/16"-4-1/2" 5/16"-4-1/2"	>=25 >=50 >=46 >=56	ㅍ35 >=50 >=65 >=80	>=240 >=345 >=450 >=550
AMS 4921	70,000psi Y.S	소 둔	5/16"-4-1/2"	>=56	>=80	>=550
JIS H4650	Class1 Class2 Class3	소 둔 소 둔 소 둔	8mm이상100이하 8mm이상100이하 8mm이상100이하	28-42 35-52 49-63	40-60 50-74 70-90	275-412 343-510 481-618
기 계 적 성 질
내력 (0.2% offset)			신 율 (%)		변형율 (Redcution of Area)
kgf/mm2	Ksi	Mpa(N/mm2)
>=18 >=28 >=39 >=49	>=25 >=40 >=55 >=70	>=170 >=275 >=380 >=483	>=24 >=20 >=18 >=15		>=30 >=30 >=30 >=25
>=49	>=70	>=483	>=15		>=25
>=17 >=22 >=35	>=24 >=31 >=50	>=167 >=216 >=343	>=27 >=23 >=18		- - -

- 합금 티타늄

규격	Grade	열처리조건	단면두께	기계적 성질
				인장강도	내력	신율(%)	변형율
				Mpa(N/mm2)	Mpa(N/mm2)	신율(%)	변형율
ASTM B348	Grade5 Grade7 Grade11	소 둔 소 둔 소 둔	5/16"-4-1/2" 5/16"-4-1/2" 5/16"-4-1/2"	895 >= 345 >= 240	825 >= 275 >= 170	10 >= 20 >= 24	25 >= 25 >= 30
JIS H4657 IS H4655	Class60 Class11 Class12 Class13	소 둔 소 둔 소 둔 소 둔	8mm 이상-100이하 8mm 이상-100이하 8mm 이상-100이하 8mm 이상-100이하	895 275-412 343-510 482-618	825 >=167 >=216 >=343	10 >=27 >=23 >=18